| Place of Origin: | China |
|---|---|
| Brand Name: | LUMING |
| Certification: | ISO9001, Patents,Work safety standardization certificate |
| Minimum Order Quantity: | 5 metric tons |
| Packaging Details: | Standard Export Wooden Pallet |
| Delivery Time: | Custom products 5-45 days |
| Payment Terms: | L/C, T/T, Western Union, |
| Supply Ability: | Annual Production Exceeding 120,000 Metric Tons of All Types of Refractory Materials Including Castables, Preforms, and Bric |
| Production Process: | Sintering Method | Refractoriness (℃): | 1770< Refractoriness< 2000 |
|---|---|---|---|
| Shape: | Brick | Al2O3: | 47%~72% Customizable |
| Fe2o3: | ≤0.5% | Bulk Density: | ≥2.95g/cm3 |
| Apparent Porosity: | ≤17% | Transport Package: | Export Pallet |
| Specification: | Customized Sizes Acceptable | Origin: | China |
| Highlight: | Sintering Furnace Zirconia Mullite Brick,Super Quality Zirconia Mullite Brick,Refractory Zirconia Mullite Brick |
||
Dense Refractory Brick Fused Zirconia Mullite Fire Firebricks in Good Price
Product Introduction:
Zirconia mullite brick is made of high -class zircon sand and alumina powder as raw material.After mixing,shaping,drying,sintering at high temperature shuttle kiln the zircon-mullite brick has such advantages as high bulk density, high strength, good thermal shock resistance, high temperature erosion resistance and good slag resistance.
Application:
It is mainly used in tank bottom,tank superstructure,perfume-bottle feeder,covers for working tanks and soda lime glass.
Features:
1.High density.
2.Good slag resistance.
| Item | FLMZM-11 | FLMZM-17 | FLMZM-20 | FLMZM-25 | FLMZM-30 | |
| Chemical Composition(%) | Al2O3 | ≥72 | ≥70 | ≥59 | ≥57 | ≥47 |
| ZrO2 | ≥11 | ≥17 | ≥19.5 | ≥25.5 | ≥30 | |
| SiO2 | ≤12 | ≤12 | ≤20 | ≤14.5 | ≤20 | |
| Fe2O3 | ≤0.5 | ≤0.5 | ≤0.5 | ≤0.5 | ≤0.3 | |
| Apparent Porosity(%) | ≤17 | ≤17 | ≤17 | ≤17 | ≤18 | |
| Bulk Density (g/cm3) | ≥3.1 | ≥3.15 | ≥2.95 | ≥3.15 | ≥3.10 | |
| Cold Crushing Strength (Mpa) | ≥90 | ≥90 | ≥100 | ≥120 | ≥100 | |
| 0.1Mpa Refractoriness Under Load T0.6 (ºC) | ≥1630 | ≥1650 | ≥1650 | ≥1650 | ≥1650 | |
| Permanent Linear Change On Reheating(%)1500ºCX2h | ±0.3 | ±0.3 | ±0.3 | ±0.3 | ±0.3 | |
| 20-1000ºC Thermal Expansion % (x 10-6) | 0-0.6 | 0-0.6 | 0-0.6 | 0-0.6 | 0-0.6 | |
| Thermal Conductivity (Average800ºC) W / (M.K) | ≤ 2.19 | ≤ 2.19 | ≤ 2.19 | ≤ 2.10 | ≤ 2.1 | |